cracking of a metal under combined action of tensile stress and corrosion in the presence of chlorides and an electrolyte (NACE). Starts at a pit, scratch or notch. Crack proceeds primarily along grain boundaries. The cracking process is accelerated by ch

n: the brittle failure of metals by cracking under the combined action of tensile stress and corrosion in the presence of water and hydrogen sulfide.

Cracking of a metal under the combined action of tensile stress and corrosion in the presence of water and hydrogen sulfide (a form of hydrogen stress cracking) (NACE).

n: stress developed by a material bearing a tensile load. See stress.